（广西永正工程质量检测有限公司 ，南宁 530221)

摘   要 ：研究建筑垃圾再生骨料与粉煤灰双掺混凝土在多种恶劣环境下的耐久性能 ，探讨二者协同作用机制 ，为工业固废资源化利用提供理论依据。以建筑垃圾再生骨料与粉煤灰为双掺材料制备混凝土 ，系统评估其在冻融循环 、盐性环境和酸性环境下的耐久性能。结果表明： 粉煤灰掺量为 15% 时 ，混凝土抗压强度最高 ，质量损失仅为 0. 02 g ,  耐蚀系数达 0. 996 ,  表现出最优的抗侵蚀能力与长期稳定性 ，耐久性表现良好。再生骨料掺量为 30% 时 ，混凝土在多种恶劣环境中的相对动弹性模量保持较高水平 ，结构稳定性良好：粉煤灰与再生骨料之间存在协同增强效应 ，适量粉煤灰  (15% )   可填充再生骨料界面孔隙 ，提升密实性 ；适量再生骨料  (30% )则能显著提升抗冻性与耐腐蚀性。粉煤灰与再生骨料在适量掺配下具有协同增强效应 ，可提升混凝土的密实性、抗冻性与耐腐蚀性 ，具有良好的工程应用前景。

关键词：建筑垃圾 ；粉煤灰 ；双掺混凝土 ；耐久性 ；再生骨料 ；相对弹性模量

中图分类号：TU528 . 31           文献标志码：A            文章编号： 1005- 8249  (2026)  02- 0029- 07

DOI:10. 19860/j.cnki.issn1005 - 8249.2026.02.005

 

Study on Durability of Concrete Mixed with Construction Waste and Fly Ash

YE Anli ,  WEI Riqiang

(Guangxi Yongzheng Construction Quality Test Co . ,  Ltd. ,   Nanning 530221 ,   China)

Abstract :   Study the durability performance of recycled construction waste aggregate and fly ash mixed concrete in various harsh environments ,   explore  the  synergistic  mechanism  of  the   two ,   and   provide  theoretical  basis  for  the  resource  utilization  of industrial solid waste .   Prepare  concrete  using  recycled  construction  waste  aggregates and  fly  ash as dual admixture materials , and systematically evaluate its durability performance under freeze - thaw cycles ,   saline environments ,   and acidic environments . The results showed that when the fly ash content was  15% ,   the  compressive  strength of concrete was  the highest ,   with  a mass loss of only 0. 02  g  and  a corrosion resistance coefficient of 0. 996 ,  exhibiting the best corrosion resistance and long -  term stability ,   and good durability.   When the content of recycled aggregate is 30% ,   the relative dynamic elastic modulus of concrete remains at a high level in various harsh environments ,   and the  structural  stability  is  good.   There  is  a  synergistic  enhancement effect between fly  ash  and  recycled aggregate ,   and an appropriate amount of  fly ash   (15% )   can  fill the interface pores of recycled aggregate to improve compactness;  Moderate recycled aggregate  (30% )   can  significantly improve frost resistance  and corrosion resistance .   Fly  ash  and recycled aggregates have a synergistic  enhancement effect when mixed in appropriate amounts , which  can  improve  the  compactness ,   frost   resistance ,   and   corrosion   resistance   of   concrete ,   and   have   good   engineering application prospects .

Key words :  construction waste;  fly ash;  binary - blended concrete;  durability;  recycled aggregate;  relative elastic modulus