PDF全文阅读

张天旭^{1 ,2} ,  柳    鹏^{1 ,2}  ,  姜春萌^1 ,2  ,  王    攀^1 ,2  ,  郑    斐^1 ,2  ,   张瑜硕¹  ,  宋育贤¹

 

( 1 .  新疆农业大学 水利与土木工程学院 ，乌鲁木齐 830052 ;

2.  新疆水利工程安全与水灾害防治重点实验室 ，乌鲁木齐 830052)

摘   要 ：为了探究地聚物混凝土不同养护方式对其强度的影响规律。通过试验 ，分别研究了不同水胶比和不同钢纤维掺量的地聚物混凝土在标准养护 、覆膜养护 、干燥空气养护和组合养护四种条件下的抗压强度规律，并从微观尺度对其水化行为进行了对比分析。结果表明：标准养护和覆膜养护初期能有效促进地聚物混凝土的水化反应 ，形成更为致密的凝胶体结构 ，从而显著提高抗压强度 ；干燥空气养护则因水分蒸发过快 ，导致水化不完全 ，孔隙率增加 ，抗压强度相对较低 ；组合养护则表现出较好的强度发展趋势 ，初期养护条件对后续强度发展具有显著影响 ，其中覆膜养护 3 d 后转为干燥空气养护的试件 ，其强度发展相较其他组试样表现最好 ；较低的水胶比和钢纤维的掺入对地聚物混凝土抗压强度也起着较为重要的作用。研究结果可为相关应用提供参考。

关键词：地聚物混凝土 ；养护方式 ；抗压强度 ；钢纤维

中图分类号：TU528 . 0           文献标志码：A            文章编号： 1005- 8249   (2026)  02- 0008- 07

DOI:10. 19860/j.cnki.issn1005 - 8249.2026.02.002

 

Study on the Effect of Curing Methods on the Compressive Strength of Geopolymer Concrete

ZHANG Tianxu1 , 2  ,  LIU Peng1 , 2  ,  JIANG Chunmeng1 , 2  ,  WANG Pan1 , 2  ,  ZHENG Fei 1 , 2  ,

ZHANG Yushuo1  ,  SONG Yuxian1

( 1 . College of Hydraulic and Civil Engineering ,  Xinjiang Agricultural University ,  Urumqi 830052 ,  China;

2. Xinjiang Key Laboratory of Hydraulic Engineering Security and Water Disasters Prevention ,

Urumqi 830052 ,  China)

Abstract :  To investigate the influence of different curing methods on the strength of geopolymer concrete .   Through experiments , the compressive strength  of  geopolymer  concrete  with  different  water -  glue  ratios  and  different  steel fiber content under  four conditions :  standard curing ,  film curing ,  dry air curing and combined curing were studied ,  and the hydration behavior of the concrete was  compared  and  analyzed  from  the  microscopic  scale .    The  results  show  that the hydration reaction of  geopolymer concrete can be effectively promoted  in the  early  stage  of  standard  curing  and  film  curing ,   and  a  denser  gel  structure  can  be formed ,  thereby  significantly  improving  the  compressive   strength .    Dry  air  curing  leads  to  incomplete  hydration ,   increased porosity ,   and relatively low compressive strength due to rapid evaporation of water.   The initial curing conditions had a significant impact on the  subsequent  strength  development ,   and  the specimens  that  were converted to dry air  curing after  3 days of  film curing had the best strength development compared with other groups .   The  low  water - glue  ratio  and  the  incorporation  of  steel fibers also play an important role in the compressive strength of geopolymer concrete .   Research findings  can provide references for related applications .

Key words :  geopolymer concrete;  curing method;  compressive strength;  steel fiber

项目来源：新疆维吾尔自治区自然科学基金项目  (2022D01 B104) 。

作者简介： 张天旭  (2003—) ,  男 ，本科 ，研究方向：水工材料。

通信作者： 姜春萌  (1993—) ,  男 ，博士 ，副教授 ，硕士生导师 ，研究方向：新型建筑材料相关研究。

收稿日期：2024 - 12 - 06