摘   要 ：为了践行低碳环保政策 ，减少磷尾矿资源的堆积 ，增加磷尾矿资源的合理利用。通过对碱激发磷尾矿胶凝材料的凝结时间 、力学性能 、组成特征 、微观结构和水化热五种方法 ，对其力学性能做出判断。结果表明：碱激发对磷尾矿胶凝材料凝结时间影响与激发剂的类型密切相关。PTSC 配比比 PTSS 配比初凝时间平均减少 92 min ,  PTSC 配比的终凝时间随着氢氧化钠比例减少而延长 ，PTSS 配比的终凝时间随着碳酸钠比例减少而缩短。在复合激发条件下 ，氢氧化钠与硅酸钠的复合激发效果比碳酸钠与硅酸钠的混合激发效果好 ，形成的产物更丰富 、结构更密实。在氢氧化钠与硅酸钠混合比例为 1 : 6 时效果最好。不同碱激发剂配比对磷尾矿水化热的影响变化不大 ，磷尾矿极大的抑制了水化热的发生。所以碱激发可以促进磷尾矿力学性能的提升 ，尤其在使用硅酸钠和氢氧化钠混合激发时尤为明显。研究结果可为相关应用提供参考。

关键词：磷尾矿 ；碱激发 ；微观结构 ；水化 ；胶凝性能

中图分类号：TU526           文献标志码：A            文章编号： 1005- 8249   (2026)  02- 0021- 08

DOI:10. 19860/j.cnki.issn1005 - 8249.2026.02.004

 

Influence of Alkali Activation on the Gelling Properties of Phosphorus Tailings

WANG Hao ,  GU Bingwei ,  WANG Jingzheng

(Jiangsu Ocean University ,  Lianyungang 222000 ,  China)

Abstract :  In order to implement the low - carbon and environmental protection policy ,  reduce the accumulation of phosphorus tailings  resources   and  increase  the  rational  utilization  of  phosphorus   tailings  resources ,   this  paper  judges   the  mechanical properties of  alkali  -  activated   phosphorus  tailings   cementitious  materials  through  five  methods :   setting  time ,   mechanical properties ,  composition characteristics ,  microstructure and hydration heat.   The  results  show  that the effect of alkali  activation on the setting time of phosphorus tailings cementitious materials is closely related to the type of activator.   The initial setting time

of the PTSC  ratio  is  on average  92  minutes  shorter  than that of  the PTSS ratio .    The  final  setting time  of  the  PTSC  ratio  is prolonged with the decrease of the sodium hydroxide  ratio ,  while  the final  setting time  of the  PTSS  ratio  is  shortened  with  the decrease of the sodium carbonate ratio .   Under  the  condition  of composite  activation ,   the  composite  activation  effect  of sodium

hydroxide and  sodium  silicate  is  better  than that of  sodium  carbonate and  sodium silicate ,   and the formed products  are more abundant and the structure  is  more  compact.   The  best  effect  is achieved  when  the  mixed  ratio of  sodium  hydroxide  and  sodium silicate is 1 : 6 .   The  influence of different alkali activator ratios on the hydration heat of phosphorus tailings is not significant ,   and

phosphorus tailings greatly inhibit the occurrence of hydration heat.   Therefore ,   alkali  activation  can  promote  the  improvement  of the mechanical  properties  of phosphorus  tailings ,   especially  when   sodium  silicate   and  sodium  hydroxide   are  used.    Research findings can provide references for related applications .

Key words :  phosphate tailings;  alkali activation;  microstructure;  hydration;  cementing performance