PDF全文阅读

化思瑜 ， 贾   嘉

（云南航空产业投资集团有限责任公司 ，昆明 650211)

摘   要 ：为降低混凝土路面水泥用量 ，采用矿渣粉大比例替代水泥 ，开展了不同矿渣粉  (20% 、30% 、 40% )  和钢纤维  (0. 5% 、1 . 0% 、1 . 5% )  复掺对混凝土抗压 、劈裂抗拉 、抗折强度以及耐磨性能 、吸水率的影响规律。结果表明：矿渣粉延缓早期水化反应 ，导致 28 d 力学强度降低 ，但 90 d 力学强度显著增大 ；低掺量 ( ≤1 . 0% )  钢纤维增强作用不足 ，甚至劣化力学强度及耐磨性能 ，掺量为 1 . 5% 时增强效应最为显著 ；矿渣粉可提升抗压强度和耐磨性能 ，但会降低抗折强度 ，且劈裂抗拉强度 、吸水率呈先增强后劣化趋势 ；40% 矿渣粉和1 . 5% 钢纤维复掺 ，抗压强度提高 38. 4% 、磨损深度降低 14. 1% ;  20% 矿渣粉和 1 . 5% 钢纤维复掺劈裂抗拉 、抗折强度提升最显著 ，分别提高 46. 2% 、27. 9% 。研究结果可为制备低碳 、高强度混凝土路面提供依据。

关键词：矿渣粉 ；钢纤维 ；混凝土 ；力学强度 ；耐磨性能 ；吸水率

中图分类号：TU528 . 01            文献标志码：A            文章编号： 1005- 8249  (2026)  02- 0061- 06

DOI:10. 19860/j.cnki.issn1005 - 8249.2026.02.010

 

Analysis of the Effects of Blast Furnace Slag Powder and Steel Fiber Content on

the Mechanical Properties and Abrasion Resistance of Concrete

HUA Siyu ,  JIA Jia

(Yunnan Aviation Industry Investment Group Co . ,  Ltd . ,  Kunming 650211 ,  China)

Abstract :  To  reduce   cement  usage  in  concrete  pavements ,   slag   powder  was   employed   as   a   high  -  proportion   cement replacement.   The  study  investigated the  effects of different slag powder dosages  (20% ,   30% ,  40% )  and  steel fiber content (0. 5% ,   1 . 0% ,   1 . 5% )  on  concrete  compressive  strength ,   splitting  tensile  strength ,   flexural  strength ,   abrasion  resistance , and water absorption rate .   Results  indicate :   - Blast  furnace  slag  powder retards  early  hydration  reactions ,   reducing 28 - day mechanical strength but  significantly  increasing  90  - day  mechanical  strength;   Low  steel  fiber content   (  ≤ 1 . 0% )   provided insufficient reinforcement ,  even degrading mechanical strength and abrasion resistance ,  while the reinforcement effect was most pronounced at 1 . 5%  content;   Slag powder enhanced compressive strength and abrasion resistance but reduced flexural strength , with splitting tensile strength and water absorption initially improving then deteriorating;  The  combined use of 40%  slag powder and 1 . 5%  steel fibers  increased compressive strength by 38. 4%  and reduced wear depth by 14. 1% .   The  combination  of 20% slag powder and 1 . 5%   steel fibers  showed  the  most  significant  improvement  in  splitting  tensile  strength  and  flexural  strength , increasing them by 46. 2%  and 27. 9% ,   respectively.   This  study  provides  a  basis  for preparing low - carbon ,   high - strength concrete pavements .

Key words :  slag powder;  steel fiber;  concrete;  mechanical strength;  wear resistance;  water absorption rate