摘   要 ：随着钢结构日益增多，钢管混凝土结构因管内混凝土收缩引起的脱空一直是工程界的难题，本研究依托北京市昌平区大型商业建筑 Y 型钢管柱，通过优选原材料品种 、掺加高性能膨胀剂和优质矿物掺合料、使用缓凝型减水剂对钢管混凝土配合比进行了优化研究，得到了钢管混凝土的配合比一系列优化研究数据。结果表明： 当膨胀剂掺量为 8% 时，混凝土的工作性能优异，满足钢管混凝土浇筑施工要求 ；密闭状态下混凝土的  自由膨胀率和限制膨胀率在 7 d 最大 ，14 d 趋于稳定，混凝土的膨胀值可抵抗混凝土的收缩，钢管混凝土综合性  能最优。当膨胀率掺量为 8% 时，钢管混凝土的管壁与核心混凝土贴合密实，未产生脱空。优化后的配合比可用于实际工程。

关键词：钢管混凝土 ；配合比 ；膨胀剂 ；限制收缩 ；应变

中图分类号：TU528           

文献标志码：A            

文章编号： 1005- 8249   (2025)  01- 0039- 06 

DOI:10. 19860/j.cnki.issn1005 - 8249.2025 .01 .008

 

JIAO Liying^{1 , 2},  SONG Shaomin¹ ,  MA Yongsheng³ ,  ZHANG Quangui²

(1 . Beijing Key Laboratory of Building Structure and Environmental Remediation Functional Materials ,

Beijing University of Civil Engineering and Architecture ,  Beijing 100044 ,  China;  2. Beijing Key

Laboratory of Cement Concrete Energy Saving and Waste Recycling Technology ,  Beijing 100096 ,  China;

3 . Beijing Institute of Building Materials Industry Information Technology ,  Beijing 100005 ,  China)

Abstract :  With the increasing number of steel structures ,  the problem of voids caused by the shrinkage of concrete inside the steel tube concrete structure has always been a challenge in the engineering field .   This  study relies  on the Y - shaped steel tube columns of large commercial buildings in Changping District ,  Beijing ,  and optimizes the mix proportion of steel tube concrete by selecting raw  material  varieties ,  adding  high - performance  expansion  agents  and  high - quality  mineral  admixtures ,   and  using retarding water reducers .   A series of optimization data for the mix proportion of steel tube concrete have been obtained.    The results show that when the dosage of expansion agent is 8% ,  the workability of concrete is excellent and meets the requirements of steel tube concrete pouring construction;  The free  expansion rate  and restricted expansion rate of concrete in a closed state reach their maximum at 7 days and tend to stabilize at 14 days .   The expansion value of concrete can resist the  shrinkage of concrete ,   and the comprehensive performance of steel tube concrete is optimal .   When the expansion rate is 8% ,   the wall of the steel tube concrete is

tightly adhered to the core concrete ,  no void occurred.   The  optimized mix ratio can be used in practical  engineering. 

Key words :  concrete filled steel tube;  mix proportion;  expander;  restricted contraction;   strain