摘   要 ：为探究粉煤灰基蒸压加气混凝土的毛细吸水特性 ，通过毛细吸水试验 ，分析干密度级别 、硅质材料和干燥温度对蒸压加气混凝土毛细吸水系数的影响。结果表明：在不同干密度级别中 ，B06 级粉煤灰基蒸压加气混凝土的毛细吸水系数最高 ，其次是 B05 级 ，而 B07 级最低 ；B06 级粉煤灰基蒸压加气混凝土具有较小且不均匀的孔径和较多的连通孔 ，表现出更强的毛细吸水能力 ；硅质材料类型的不同也导致了毛细吸水系数的差异，其中砂基蒸压加气混凝土的毛细吸水系数低于粉煤灰基蒸压灰加气混凝土 ，这与砂基蒸压加气混凝土中水化产物的结晶度较高 ，减少了毛细孔的数量有关 ；干燥温度的升高对毛细吸水系数有一定的促进作用 ，但相较于普通混凝土 ，这种影响在粉煤灰基蒸压加气混凝土中并不显著。

关键词：蒸压加气混凝土 ；毛细吸水特性 ；干密度级别 ；硅质材料 ；干燥温度

中图分类号：TU528           文献标志码：A            文章编号： 1005- 8249   (2026)  01- 0063- 05

DOI:10. 19860/j.cnki.issn1005 - 8249.2026.01 .012

WANG Xiaobing¹  ,  ZHANG Chuanda¹  ,  GAO Jian¹  ,  GAN Yuannan² ,  JI Yunfeng²

( 1 . Henan Luoning Pumped Storage Co . ,  Ltd . ,  Luoyang 471000 ,  China;

2. China Anneng Group Second Engineering Bureau Co . ,  Ltd . ,  Nanchang 330096 ,  China)

Abstract :  In order to investigate the capillary water absorption characteristics of fly ash - based autoclaved aerated concrete ,  the effects of dry density level ,  siliceous material and drying temperature on the capillary water absorption coefficient of autoclaved aerated concrete were analyzed by carrying out capillary water absorption tests .   The  test  results  show  that  among  different  dry density grades ,  the  capillary  water  absorption  coefficient  of  fly  ash -  based  autoclaved  aerated  concrete  of  grade  B06  is  the highest ,  followed by  grade  B05 ,   while  grade  B07   is  the  lowest.    SEM  electron  microscopy  analysis  reveals  that  grade  B06 exhibits a stronger capillary water absorption capacity due to its  smaller and uneven pore  size  and  more  connecting pores .   The difference in the type of siliceous  material also affects the difference in the capillary water absorption coefficient ,  with  sand - based autoclaved aerated concrete  having a lower capillary water absorption  coefficient  than  fly  ash - based  autoclaved  aerated concrete .   This  is  attributed to the higher crystallinity of hydration products in sand - based  autoclaved  aerated concrete ,  which reduces the number of capillary pores .   Additionally ,   an  increase  in drying temperature promotes the capillary water absorption coefficient;  however ,  this effect is not significant in fly ash - based autoclaved aerated concrete  compared to ordinary concrete This is because temperature  changes  below  100  ℃  have a limited impact on the microstructure of  fly  ash - based autoclaved aerated concrete .

Key words :  autoclaved aerated concrete;  capillary water absorption;  dry density grades;  siliceous materials;  drying temperature