马建平

 

（宁夏理工学院 建筑与环境学院 ，石嘴山   753000)

   摘   要 ：为获得粉煤灰渣替代天然河砂后混凝土性能的变化规律 ，通过室内试验 ，制备与天然河砂相同颗粒级配的粉煤灰渣 ，以等体积原则替代天然河砂 ，研究粉煤灰渣替代率对混凝土强度及耐久性的影响 ，并分粉煤灰渣与水泥之间强度演变机理。结果表明： 粉煤灰渣替代天然河砂后混凝土的抗压强度 、抗折强度随替代率增加呈先增大后减小趋势 ，替代率为 50% 时 ，混凝土的抗压强度 、抗折强度提高最显著 ；随粉煤灰渣替代率增长 ，混凝土的碳化深度先减小后增大 ，替代率为 50% 时碳化深度最小 ；掺入粉煤灰渣后降低了混凝土的抗渗性能 ，抗渗等级随替代率增加而减小 ；粉煤灰渣内部的水分可提高其周边水泥的水化程度 ，提高结构致密程度，水泥与粉煤灰渣表面活性成分水化产生水化硅酸钙 ，增强与粉煤灰渣之间的握裹力。

关键词：粉煤灰渣 ；细骨料 ；混凝土 ；强度 ；耐久性

中图分类号：TU521            文献标志码：A           文章编号： 1005- 8249   (2026)  01- 0001- 06

DOI:10. 19860/j.cnki.issn1005 - 8249.2026.01 .001

 

MA Jianping

(College of Architecture and Environment ,  Ningxia Institute of Science and

Technology ,  Shizuishan 753000 ,  China)

Abstract :  In order to obtain the change rule of concrete performance after replacing natural river sand with fly ash slag ,  through indoor test ,  prepare fly  ash  slag with  the  same  particle  gradation  as  natural  river  sand ,  replace  natural  river  sand  with  equal volume principle ,  study the effect of fly  ash  slag substitution rate  on the  strength  and  durability  of concrete ,  and  analyze the mechanism of strength evolution between fly ash slag and cement.  The  results  show that :  the compressive strength and flexural strength of concrete after replacing natural river sand by fly ash slag shows a tendency of increasing and then decreasing with the increase of substitution rate ,  and when the substitution rate is 50% ,  the compressive strength and flexural strength of concrete are most significantly improved;  with the increase of substitution rate of fly ash slag ,  the carbonation depth of concrete decreases and then  increases ,  and  when  the  substitution  rate  is  50% ,  the  carbonation  depth  is  the  smallest;  the  impermeability performance of concrete is reduced by the addition of fly ash slag ,  and the impermeability grade increases with the substitution rate of 50% .  Performance ,  impermeability grade decreases with the increase of substitution rate;  Fly ash slag internal moisture can improve the hydration of the cement around it ,  to improve the degree of structural densification ,  the cement and fly ash slag surface active ingredient hydration produces hydrated calcium silicate ,  to enhance and fly ash slag between the grip force .

Key words :  fly ash slag;  fine  aggregate;  concrete;   strength;  durability