PDF全文阅读

郝利斌¹ ,  董泽彬² ,  郭   峰¹

 

( 1 .  华冠天诚检测认证有限公司 ，太原 030000 ;  2.  西南交通大学 ，成都 611730)

摘   要 ：为了提高铁尾矿的利用效率 ，并降低混凝土材料的生产成本 ， 以铁尾矿砂取代部分天然砂作为细骨料 ，并掺入钢纤维 ，制备出了铁尾矿－钢纤维复合粉煤灰基混凝土。通过抗压强度和劈裂抗拉强度试验评价了铁尾矿和钢纤维掺量对混凝土力学性能的影响 ，通过碳化试验和盐雾侵蚀试验评价了混凝土的耐老化性能。结果表明：钢纤维的长度和掺量越大 ，铁尾矿砂的掺量越大时 ，混凝土的抗压强度和劈裂抗拉强度均先升高后降低 ，当钢纤维的长度为 35 mm ,  掺量为 1 . 5% ,  铁尾矿砂的掺量为 40% 时 ，混凝土的力学性能达到最佳 ，抗压强度和劈裂抗拉强度分别为 30. 08 、6. 64 MPa。铁尾矿－钢纤维复合混凝土的耐老化性能较好 ， 当碳化龄期和盐雾侵蚀龄期达到 56 d 时 ，混凝土的碳化深度为 12. 8 cm ,  碳化试验后的抗压强度为 36. 72 MPa ,  盐雾侵蚀试验后的抗压强度为 29. 51 MPa。

关键词：铁尾矿 ；钢纤维 ；粉煤灰基混凝土 ；力学性能 ；耐老化性能

中图分类号：TU528           文献标志码：A           文章编号： 1005- 8249   (2026)  01- 0037- 06

DOI:10. 19860/j.cnki.issn1005 - 8249.2026.01 .007

HAO Libin¹  ,  DONG Zebin² ,   GUO Feng¹

( 1 . Huaguan Tiancheng Testing and Certification Co . ,   Ltd. ,  Taiyuan 030000 ,   China;

2. Southwest Jiaotong University ,   Chengdu 611730 ,   China)

Abstract :   In order to improve the utilization efficiency of iron tailings and reduce the production cost of concrete materials ,   iron tailings sand was used to replace some natural sand as fine aggregate ,   and steel fibers were added to prepare iron tailings steel fiber composite fly ash based concrete.   The influence of iron tailings and steel fiber content on the mechanical properties of concrete was evaluated through  compressive  strength and splitting tensile strength tests ,    and  the  aging resistance of  concrete was evaluated through carbonation tests and salt spray erosion tests .   The results  showed that as the length and dosage of steel fibers  increased and the dosage of iron tailings sand increased ,   the compressive strength and splitting tensile strength of concrete first increased and then decreased.   When  the  length of steel fibers was 35mm ,   the  dosage of steel fibers was 1 . 5% ,   and the  dosage of iron tailings sand was 40% ,  the mechanical properties of concrete reached their optimum ,  with compressive strength and splitting tensile strength of30. 08 、6. 64   MPa ,   respectively.    The   aging   resistance   of   iron   tailings   steel  fiber  composite   concrete   is   good.    When   the carbonation age and salt spray erosion age reach 56 days ,   the carbonation depth of the concrete is  12. 8  cm ,   and  the compressive strength after carbonation test is 36. 72 MPa ,   and the compressive  strength after salt spray erosion test is 29. 51  MPa.

 Key words :  iron tailings;  steel fiber;  fly ash based concrete;  mechanical properties;  aging resistance

作者简介：郝利斌  (1989—) ,  男 ，本科 ，高级工程师 ，研究方向：试验检测。

通信作者：董泽彬  (2005—) ,  男 ，本科在读 ，研究方向：材料科学与工程。

收稿日期：2025 - 10 - 24