摘   要 ：为缓解大量废弃磷石膏对环境的污染 ， 同时降低传统高能耗水泥的消耗。以磷石膏 、水泥 、微硅粉 、硫铝酸盐水泥 、熟石灰为主要原材料外掺减水剂制备磷石膏水泥基复合材料及泡沫轻质材料 ，通过复合材料单因素试验 ，确定复合材料最优配合比 ，再以复合材料最优配合比为基准配合比制备泡沫轻质材料 ，研究磷石膏掺量 、水固比和泡沫掺量对泡沫轻质材料性能的影响 ，结果表明：磷石膏水泥基泡沫轻质材料满足使用要求的磷石膏最大掺量为 60% ,  水固比以 0. 4 ~ 0. 5 为宜 ，满足使用要求的泡沫掺量为 4% ~ 7% 。因此在实际工程中可制备磷石膏掺量 60% 的磷石膏水泥基泡沫轻质材料用于路基填筑。

关键词：磷石膏 ；复合材料 ；泡沫轻质材料 ；湿密度 ；抗压强度

中图分类号：U414           

文献标志码：A            

文章编号： 1005- 8249   (2025)  05- 0072- 07

DOI:10. 19860/j.cnki.issn1005 - 8249.2025 .05 .014

 

ZHOU Jichen1  ,  JIANG Tao2 ,  ZOU Tao3

（1 . Nantong Municipal Urban Construction Engineering Management Center ,  Nantong 226000 ,  China;

2. Jiangsu Shuangning Eengineering Consulring Co . ,  Ltd . ,  Nanjing 211212 ,  China;

3 . Wuxi Xishan Houqiao Water Conservancy Management Station ,  Wuxi 214000 ,  China)

Abstract :  In order to alleviate the environmental pollution caused by a large amount of discarded phosphogypsum  ( PG)  and reduce the consumption of traditional high - energy cement. PG  cement - based  composites  and  foam  lightweight  materials  are prepared with PG , cement , micro  silica  powder , sulphoaluminate  cement  and hydrated lime  as  the  main raw materials  and water reducer. Through  the single  factor  test  of  composite  materials , the  optimal  mix  proportion  of composite  materials is determined ,  and then foam  lightweight  materials  are  prepared  with  the  optimal  mix proportion  of  composite  materials  as  the benchmark mix proportion. The effects of PG content , water solid ratio and foam content on the performance of foam lightweight materials are studied . The results  show that the  maximum PG content of PG cement - based foam lightweight materials that meet the use requirements is 60% ,  the water solid ratio is 0. 4 ~ 0. 5 , and the foam content that meets  the use requirements is 4% ~ 7% . Therefore , PG cement  based  foam  lightweight  material  with  60%  PG  content  can  be  prepared  for  subgrade  filling  in practical projects .

Key words :  phosphogypsum;  composites;  foam lightweight materials;  wet density; compressive  strength