摘   要 ：为实现废旧混凝土再生细骨料的高值化利用，研究了不同泡沫掺量、聚丙烯纤维掺量对再生细骨料泡沫混凝土的湿密度、流动度、抗压强度等工作性能影响，结合多种拟合形式分析了泡沫掺量与抗压强度之间的拟合关系。结果表明： 随泡沫掺量的增加，再生细骨料泡沫混凝土的湿密度明显下降、流动度减小、抗压强度降低；对不同泡沫掺量的再生细骨料泡沫混凝土，聚丙烯纤维的掺入会对湿密度与流动度产生不同影响，对抗压强度无明显改善效果；根据有无聚丙烯纤维掺入，再生细骨料泡沫混凝土的泡沫掺量与强度最佳拟合形式分别为指数拟合和多项式拟合。

关键词：再生细骨料 ；泡沫混凝土 ；抗压强度 ；泡沫掺量 ；聚丙烯纤维

中图分类号：U414           

文献标志码：A            

文章编号： 1005- 8249   (2025)  01- 0001- 06 

DOI:10. 19860/j.cnki.issn1005 - 8249.2025 .01 .001

CAI Yanxia^{1 , 2 , 3}  ,  LUO Shuai ¹  ,  QIU Wei⁴ ,  GAO Jiaqi², ³ ,  XUE Xiaojie⁴ ,  LI Lihui³

(1 . School of Civil Engineering ,  Hebei University of Engineering ,  Handan 056038 ,  China;

2. Beijing Zhonglu Gaoke Highway Technology Co.，Ltd. ，Beijing 100088 ,  China; 3 . Research Institute of Highway Ministry of Transport ,  Beijing 100088 ,  China;    4. Guangzhou Expressway Technology Co.，Ltd. ，Guangzhou 510000 ,  China)

Abstract：In order to achieve the high-value utilization of recycled fine aggregate from waste concrete, the study investigated the influence of different foam dosages and the presence of polypropylene fibers on the workability properties, such as wet density, flowability, and compressive strength of recycled fine aggregate foamed concrete. By combining various fitting forms, the relationship between foam dosage and compressive strength was analyzed. The research showed that with an increase in foam dosage, the wet density of recycled fine aggregate foamed concrete decreased significantly, while the flowability and compressive strength decreased. The addition of polypropylene fibers had different effects on the wet density and flowability of recycled fine aggregate foamed concrete with different foam dosages, but it did not have a significant improvement effect on compressive strength. According to the presence or absence of polypropylene fibers, the optimal fitting forms for the relationship between foam dosage and strength of recycled fine aggregate foamed concrete were exponential fitting and polynomial fitting, respectively

 Key words: recycled fine aggregates；foamed concrete；compressive strength；foam content；polypropylene fiber