摘   要 ：为分析再生骨料碳化改性性能及固碳问题，采用正交试验法对粉煤灰掺量 、再生骨料取代率及水  胶比等因素对再生混凝土抗碳化性能进行研究 ，分析再生骨料取代率的合理利用以提高再生混凝土抗碳化能力。 结果表明：再生骨料取代率 、水胶比 、粉煤灰掺量的增加会加大再生混凝土的碳化深度 ，且水胶比对碳化深度  的影响最大 ；水胶比取 0. 5 、粉煤灰掺量取 10% 、再生骨料取代率取 25% 时 ，再生混凝土抗碳化能力最强。提  高再生骨料的固碳效率 ，要合理选择摊铺方式 ，以确保固碳效果。

关键词：再生骨料 ；抗碳化性能 ；固碳效果

中图分类号：TU528 . 041            

文献标志码：A            

文章编号： 1005- 8249  (2024)  06- 0024- 07

DOI:10. 19860/j.cnki.issn1005 - 8249.2024.06.005

 

CHI Lingjun¹  ,  CAI Yingchun² ,  QIAO Baolei ¹  ,  ZHANG Shaobo¹  ,  CUI Hao^2 , 3

( 1 . China Construction Seventh Engineering Division. Corp. ，Ltd. ，Zhengzhou 450016 ,  China;  2. School  of

Water Conservancy and Civil Engineering ,  Zhengzhou University ,  Zhengzhou 450001 ,  China;

3 . Henan Province Highway Engineering Bureau Group Co. ，Ltd. ，Zhengzhou 450052 ,  China)

Abstract :  In order to  analyze  the  performance  of  carbonization  modification  of recycled  aggregate  and  the  problem  of  carbon fixation.   The  anti- carbonation  performance of recycled concrete was studied by using orthogonal test method ,  including fly ash content ,  recycled aggregate replacement  ratio  and  water -  binder  ratio ,   the  reasonable  utilization  of  the replacement ratio  of recycled aggregate is analyzed to improve the carbonation resistance of recycled concrete .   The  results  show  that the  carbonation depth of recycled concrete increases with the increase of the replacement ratio of recycled aggregate ,  the water- binder ratio and the content of fly ash ,  and the water- binder ratio has the greatest influence on the carbonation depth When the ratio of water to binder is 0. 5 ,   the content of fly ash is  10% ,   and  the replacement ratio of recycled aggregate  is 25% ,  the  anti- carbonation ability of recycled  concrete  is  the  best.    In  order  to  improve  the  carbon fixation  efficiency  of  recycled  aggregate ,   we  should choose reasonable spreading ways to ensure the carbon fixation effect.

Keywords:  recycled aggregate;  carbonization resistance;  carbon fixation effect